Materials Degradation in Mechanical Design: Wear, Corrosion, Fatigue, and Their Interactions Web Seminar RePlay
EDU Trainings s.r.o.
Popis kurzu
Materials degradation from environmental conditions is a common factor that will often occur in mechanical equipment used in every type of environment. These processes can frequently materialize in unpredicted and harmful ways, especially when they interact and lead to early component damage or failure.
Captured from five, two-hour sessions, this course summarizes the mechanisms that cause materials and mechanical components to degrade in service through exposure to deleterious mechanical and environmental conditions. It’s designed to develop knowledge of issues of material degradation in service and the effect upon the performance and reliability in the process of mechanical design. These processes include wear, corrosion, fatigue, and their interactions. The instructor takes a practical approach and covers potential solutions, including material selection and material or design modifications that improve component life and performance in a range of harmful environments or operating conditions. The review of each mechanism includes a presentation of the fundamental basis for these failure mechanisms, followed by practical examples of how they occur in reality.
Objectives
By participating in this course, you’ll be able to:
Cite the typical wear mechanisms that occur in mechanical equipment and their causes
Cite the basic corrosion mechanisms and their causes
Identify the interactions that occur between wear, corrosion and fatigue
Suggest practical material or design solutions to those damage mechanisms
Captured from five, two-hour sessions, this course summarizes the mechanisms that cause materials and mechanical components to degrade in service through exposure to deleterious mechanical and environmental conditions. It’s designed to develop knowledge of issues of material degradation in service and the effect upon the performance and reliability in the process of mechanical design. These processes include wear, corrosion, fatigue, and their interactions. The instructor takes a practical approach and covers potential solutions, including material selection and material or design modifications that improve component life and performance in a range of harmful environments or operating conditions. The review of each mechanism includes a presentation of the fundamental basis for these failure mechanisms, followed by practical examples of how they occur in reality.
Objectives
By participating in this course, you’ll be able to:
Cite the typical wear mechanisms that occur in mechanical equipment and their causes
Cite the basic corrosion mechanisms and their causes
Identify the interactions that occur between wear, corrosion and fatigue
Suggest practical material or design solutions to those damage mechanisms
Obsah kurzu
Session 1 – CorrosionElectrochemical cell
Galvanic series
Corrosion mechanisms:
Galvanic corrosion
Uniform attack
Session 2 – Corrosion (continued)
Corrosion mechanisms (cont.)
Crevice corrosion/pitting
Stress corrosion cracking
Effects of corrosion on component life
Corrosion solutions and prevention
Session 3 – Wear
Adhesion
Abrasion
Session 4 – Wear (continued)
Fretting
Tribo-corrosion
Fatigue wear
Erosion
Session 5 – Lubrication
Theory and application and the effects on friction and wear
Materials Provided
90 days of online single-user access (from date of purchase)
Nearly 10 hours of instructor-delivered content
Course workbook (downloadable, .pdf’s)
Online learning assessment
Instructor follow up to your content questions
1.0 CEUs*/Certificate of Achievement (upon completion of all course content and a score of 70% or higher on the learning assessment)
*SAE International is authorized by IACET to offer CEUs for this course.